New horizon in mechanochemistry—high-temperature,high-pressure mechanical synthesis in a planetary ball mill—with magnesium hydride synthesis as an example

A new route of materials synthesis, namely, high-temperature, high-pressure reactive planetary ball milling (HTPRM), is presented. HTPRM allows for the mechanosynthesis of materials at fully controlled temperatures of up to 450 °C and pressures of up to 100 bar of hydrogen. As an example of this application, a successful synthesis of magnesium hydride is presented. The synthesis was performed at controlled temperatures (room temperature (RT), 100, 150, 200, 250, 300, and 325 °C) while milling in a planetary ball mill under hydrogen pressure ($>$50 bar). Very mild milling conditions (250 rpm) were applied for a total milling time of 2 h, and a milling vial with a relatively small diameter (φ = 53 mm, V = ～0.06 dm³) was used. The effect of different temperatures on the synthesis kinetics and outcome were examined. The particle morphology, phase composition, reaction yield, and particle size were measured and analysed by scanning electron microscopy, X-ray diffraction, differential scanning calorimetry (DSC) techniques. The obtained results showed that increasing the temperature of the process significantly improved the reaction rate, which suggested the great potential of this technique for the mechanochemical synthesis of materials.     

成型温度对PBX装药内部质量及性能的影响

针对压制成型的PBX炸药装药，选择CT无损检测、巴西实验和扫描电镜检测等技术，对比研究了室温和加热两种温度下压制成型的炸药装药内部质量、静态力学性能和细观破坏形式。结果表明，加热压制有利于改善炸药装药的内部质量，可避免产生初始损伤，且提高了装药的力学性能。细观尺度上，室温压制成型的装药主要发生界面脱黏破坏，加热压制成型装药的主要破坏形式是穿晶断裂。     

Surface treatment of titanium dioxide nanopowder using rotary electrode dielectric barrier discharge reactor

Titanium dioxide (TiO2) nanopowder (P-25;Degussa AG) was treated using dielectric barrier discharge (DBD) in a rotary electrode DBD (RE-DBD) reactor.Its electrical and optical characteristics were investigated during RE-DBD generation.The treated TiO2 nanopowder properties and structures were analyzed using x-ray diffraction (XRD) and Fourier-transform infrared spectroscopy (FTIR).After RE-DBD treatment,XRD measurements indicated that the anatase peak theta positions shifted from 25.3° to 25.1°,which can be attributed to the substitution of new functional groups in the TiO2 lattice.The FTIR results show that hydroxyl groups (OH) at 3400 cm-1 increased considerably.The mechanism used to modify the TiO2 nanopowder surface by air DBD treatment was confirmed from optical emission spectrum measurements.Reactive species,such as OH radical,ozone and atomic oxygen can play key roles in hydroxyl formation on the TiO2 nanopowder surface.     

Mitochondrial and Autophagic Regulation of Adult Neurogenesis in the Healthy and Diseased Brain

Adult neurogenesis is a highly regulated process during which new neurons are generated from neural stem cells in two discrete regions of the adult brain: the subventricular zone of the lateral ventricle and the subgranular zone of the dentate gyrus in the hippocampus. Defects of adult hippocampal neurogenesis have been linked to cognitive decline and dysfunction during natural aging and in neurodegenerative diseases, as well as psychological stress-induced mood disorders. Understanding the mechanisms and pathways that regulate adult neurogenesis is crucial to improving preventative measures and therapies for these conditions. Accumulating evidence shows that mitochondria directly regulate various steps and phases of adult neurogenesis. This review summarizes recent findings on how mitochondrial metabolism, dynamics, and reactive oxygen species control several aspects of adult neural stem cell function and their differentiation to newborn neurons. It also discusses the importance of autophagy for adult neurogenesis, and how mitochondrial and autophagic dysfunction may contribute to cognitive defects and stress-induced mood disorders by compromising adult neurogenesis. Finally, I suggest possible ways to target mitochondrial function as a strategy for stem cell-based interventions and treatments for cognitive and mood disorders.     

水杨酸处理诱导采后甜瓜抗坏血酸-还原型谷胱甘肽循环代谢清除过氧化氢的作用及机制

目的：研究抗坏血酸（ascorbic acid，AsA）-还原型谷胱甘肽（reduced glutathione，GSH）循环代谢在水杨酸处理采后甜瓜诱导的过量H2O2清除过程中的作用。方法：用4 mmol/L水杨酸浸泡‘玉金香’厚皮甜瓜10 min，测定处理后果实常温贮藏过程中丙二醛（malondialdehyde，MDA）含量，分析活性氧的积累水平、超氧化物歧化酶（superoxide dismutase，SOD）和过氧化氢酶（catalase，CAT）活力，以及AsA-GSH循环过程相关酶活力及产物和底物含量。结果：水杨酸处理降低了果实MDA含量，第10天处理组MDA含量较对照组降低14.6%；显著提高了果实O2－·的产生速率和H2O2含量（P＜0.05），其中处理后第2天O2－·的产生速率高出同期对照组的1.9 倍，第6天H2O2含量高出对照组果实29.7%；提高了果实SOD活力，但抑制了CAT活力，说明H2O2的清除可能是依赖于除酶促系统外的其他系统。此外，水杨酸处理提高了果实抗坏血酸过氧化物酶、单脱氢抗坏血酸过氧化物酶、脱氢抗坏血酸还原酶和谷胱甘肽还原酶的活力，增加了AsA和氧化型谷胱甘肽的含量，降低了脱氢抗坏血酸和GSH的含量。结论：水杨酸处理诱导了厚皮甜瓜果实的氧爆，抑制了MDA产生，由水杨酸诱导产生的过量H2O2主要依靠AsA-GSH循环系统清除。     

Tailored-Made Polydopamine Nanoparticles to Induce Ferroptosis in Breast Cancer Cells in Combination with Chemotherapy

Ferroptosis is gaining followers as mechanism of selective killing cancer cells in a non-apoptotic manner, and novel nanosystems capable of inducing this iron-dependent death are being increasingly developed. Among them, polydopamine nanoparticles (PDA NPs) are arousing interest, since they have great capability of chelating iron. In this work, PDA NPs were loaded with Fe³⁺ at different pH values to assess the importance that the pH may have in determining their therapeutic activity and selectivity. In addition, doxorubicin was also loaded to the nanoparticles to achieve a synergist effect. The in vitro assays that were performed with the BT474 and HS5 cell lines showed that, when Fe³⁺ was adsorbed in PDA NPs at pH values close to which Fe(OH)₃ begins to be formed, these nanoparticles had greater antitumor activity and selectivity despite having chelated a smaller amount of Fe³⁺. Otherwise, it was demonstrated that Fe³⁺ could be released in the late endo/lysosomes thanks to their acidic pH and their Ca²⁺ content, and that when Fe³⁺ was co-transported with doxorubicin, the therapeutic activity of PDA NPs was enhanced. Thus, reported PDA NPs loaded with both Fe³⁺ and doxorubicin may constitute a good approach to target breast tumors.     

Novel TiC-based composites with enhanced mechanical properties

Novel TiC-based composites were synthesized by reactive hot-pressing at 1800 °C for 1 h with ZrB₂ addition as a sintering aid for the first time. The effects of ZrB₂ contents on the phase composition, microstructure evolution, and mechanical properties were reported. Based on the reaction and solid solution coupling effects between ZrB₂ and TiC, the product ZrC may be partially or completely dissolved into the TiC matrix, and then phase separation within the miscibility gap is observed to form lamellar nanostructured ZrC-rich (Zr, Ti)C. The TiC-10 mol.% ZrB₂ (starting batch composition) exhibits good comprehensive mechanical properties of hardness 27.7 ± 1.3 GPa, flexural strength 659 ± 48 MPa, and fracture toughness of 6.5 ± 0.6 MPa m^1/2, respectively, which reach or exceed most TiC-based composites using ceramics as sintering aids in the previous reports.     

Pectic Galactan Polysaccharide-Based Gene Delivery System for Targeting Neuroinflammation

Treating neuroinflammation-related injuries and disorders through manipulation of neuroinflammation functions is being heralded as a new therapeutic strategy. In this study, a novel pectic galactan (PG) polysaccharide based gene therapy approach is developed for targeting reactive gliosis in neuroinflammation. Galectin-3 (Gal-3) is a cell protein with a high affinity to β-galactoside sugars and is highly expressed in reactive gliosis. Since PG carries galactans, it can target reactive gliosis via specific carbohydrate interaction between galactan and Gal-3 on the cell membrane, and therefore can be utilized as a carrier for delivering genes to these cells. The carrier is synthesized by modifying quaternary ammonium groups on the PG. The resulting quaternized PG (QPG) is found to form complexes with plasmid DNA with a mean diameter of 100 nm and have the characteristics required for targeted gene therapy. The complexes efficiently condense large amounts of plasmid per particle and successfully bind to Gal-3. The in vivo study shows that the complexes are biocompatible and safe for administration and can selectively transfect reactive glial cells of an induced cortical lesion. The results confirm that this PG-based delivery system is a promising platform for targeting Gal-3 overexpressing neuroinflammation cells for treating neuroinflammation-related injuries and neurodegenerative diseases.     

Fabrication and laser performances of Yb:Sc2O3 transparent ceramics from different combination of vacuum sintering and hot isostatic pressing conditions

In this paper we report on the preparation and laser performance of transparent 3at.% Yb:Sc₂O₃ ceramics by reactive sintering of commercially available powders under vacuum followed by hot isostatic pressing (HIP). Combinations of different vacuum sintering temperatures (1650 °C and 1750 °C) and different HIP treatments (1700 °C and 1800 °C at 200 MPa) were tested in order to understand how these steps influence the microstructure and thus the optical and lasing properties of the ceramic samples. All the samples showed a good optical quality. The microstructure analysis and the laser tests showed that the vacuum pre-sintering temperature is the key factor determining the quality of the samples and the laser performances. The best values of slope efficiency i.e. η_L = 50 % and output power i.e. P_out = 6.62 W were obtained for the sample pre-sintered under vacuum at 1650 °C and hot isostatically pressed at 1800 °C.     

热处理对挤压态Mg-6Gd-5Y-1Zn合金组织与性能的影响

通过对Mg-6Gd-5Y-1Zn(质量分数,%)合金在固溶和时效处理状态下显微组织和力学性能的研究发现,α-Mg基体、沿挤压方向分布的条状18R-LPSO相、少量的Mg₂₄(GdYZn)₅ 相以及细层片状的14H-LPSO相构成了挤压态合金的组成相。挤压态合金经固溶(T4)处理后,一部分18R-LPSO相溶入基体,并且基体中的14H-LPSO相伸长同时粗化。挤压态合金经过固溶加时效(T6)处理后,大量β′相从α-Mg基体中析出。T6态合金的室温力学性能最好,其屈服强度、抗拉强度及伸长率分别为272 MPa、406 MPa和6.1%。β′相沉淀也发生在挤压态合金的直接人工时效(T5)处理过程,但相比于T6处理,14H-LPSO相和β′相在基体中的体积分数均偏低。